- 密度 [g/cm3]: 0.637
- 拉伸強度 [MPa]: 3.07
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.637 g/cc | 0.0230 lb/in3 | ASTM D1667 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore O | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 3.07 MPa | 445 psi | ASTM D3574 |
| Elongation at Break | 300 % | 300 % | ASTM D3574 |
| Tensile Modulus | 0.00172 GPa | 0.250 ksi | ASTM D3574 |
| Compressive Strength | 0.448 MPa | 65.0 psi | Compression Deflection, Value given for 12.7 mm/min, 25% deflection.; ASTM D3574 Test C |
| Compressive Modulus | 0.000758 GPa | 0.110 ksi | Force to Compress, Value given for 25% compression; ASTM D1667 |
| Coefficient of Friction, Dynamic | 1.4 | 1.4 | ASTM D4518 |
| Tear Strength | 10.5 kN/m | 60.0 pli | Initial Tear Strength; ASTM D624 Die C |
| Compression Set | <= 5.0 % | <= 5.0 % | Constant Deflection at 73°F; ASTM D 3574 Test D |
| <= 35 % @Temperature 70.0 °C | <= 35 % @Temperature 158 °F | Constant Deflection; ASTM D 3574 Test D | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Constant use |
| 121 °C | 250 °F | Intermittent | |