- 密度 [g/cm3]: 1.3
- 拉伸強度 [MPa]: 0.19
- 彎曲強度 [MPa]: 0.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 0.860 MPa | 125 psi | 500 mm/min; ASTM D412 80 |
| Tensile Strength, Yield | 0.190 MPa @Strain 100 % | 27.6 psi @Strain 100 % | ASTM D412 80 |
| Elongation at Break | 500 % | 500 % | 500 mm/min; ASTM D412 80 |
| Compressive Yield Strength | 0.610 MPa | 88.5 psi | 50% strain; ASTM D575 Method A |
| Resilience | 13.2 | 13.2 | Lupke rebound test |
| Coefficient of Friction | 2.6 | 2.6 | on polished steel; ASTM D1894 |
| Coefficient of Friction, Static | 10.4 | 10.4 | on polished steel; ASTM D1894 |
| Tear Strength Test | 23.5 | 23.5 | psi per ASTM 624 with 1 mm nick |
| Compression Set | 6.2 % | 6.2 % | 72 hr/73°F/25% compression - ASTM 395 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 132 μm/m-°C @Temperature -50.0 - 100 °C | 73.3 μin/in-°F @Temperature -58.0 - 212 °F | |
| Thermal Conductivity | 0.380 W/m-K | 2.64 BTU-in/hr-ft2-°F | estimated from other durometer grades |
| Maximum Service Temperature, Air | <= 82.0 °C | <= 180 °F | Optimum performance range |
| Minimum Service Temperature, Air | >= -29.0 °C | >= -20.2 °F | optimum performance range |
| Glass Transition Temp, Tg | -43.0 °C | -45.4 °F | |
| Flammability, UL94 | V-2 | V-2 | |