Rogers Corporation Poron? 4790-79SP-15012 Urethane Shock Pad Foam

Rogers Corporation Poron? 4790-79SP-15012 Urethane Shock Pad Foam 物性表: Rogers Corporation Poron? 4790-79SP-15012 Urethane Shock Pad Foam物性表及特性介紹,Rogers Corporation Poron? 4790-79SP-15012 Urethane Shock Pad Foam注塑參數(shù)詳情,如需Rogers Corporation Poron? 4790-79SP-15012 Urethane Shock Pad Foam下載, 可到相關(guān)下載區(qū)下載

密度 [g/cm3]: 0.24

Physical Properties	Metric	English	Comments

Density	0.240 g/cc	0.00868 lb/in3	ASTM D3574-95 Test A
Thickness	27.9 - 43.2 microns	1.10 - 1.70 mil	Supported Adhesive
	191 - 343 microns	7.50 - 13.5 mil	Urethane Foam
	229 - 381 microns	9.00 - 15.0 mil	Total Construction

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	78 %	78 %	ASTM D882
	74 % @Temperature 66.0 °C, Time 346000 sec	74 % @Temperature 151 °F, Time 96.0 hour	80% RH; ASTM D882
Film Elongation at Break, TD	32 %	32 %	ASTM D882
	66 % @Temperature 66.0 °C, Time 346000 sec	66 % @Temperature 151 °F, Time 96.0 hour	80% RH; ASTM D882
Compressive Yield Strength	0.0299 MPa @Strain 25.0 %	4.34 psi @Strain 25.0 %	0.2"/min. strain rate
Tear Strength	0.310 kN/m @Time 1190 sec	1.77 pli @Time 0.330 hour	Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000
	0.320 kN/m @Time 1190 sec	1.83 pli @Time 0.330 hour	Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000
	0.320 kN/m @Time 259000 sec	1.83 pli @Time 72.0 hour	Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000
	0.330 kN/m @Time 1190 sec	1.88 pli @Time 0.330 hour	Peel Adhesion, 180° Peel, to ABS; ASTM D1000
	0.330 kN/m @Time 1190 sec	1.88 pli @Time 0.330 hour	Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000
	0.340 kN/m @Time 1190 sec	1.94 pli @Time 0.330 hour	Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000
	0.360 kN/m @Time 259000 sec	2.05 pli @Time 72.0 hour	Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000
	0.390 kN/m @Time 259000 sec	2.23 pli @Time 72.0 hour	Peel Adhesion, 180° Peel, to ABS; ASTM D1000
	0.390 kN/m @Time 259000 sec	2.23 pli @Time 72.0 hour	Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000
	0.404 kN/m @Time 259000 sec	2.31 pli @Time 72.0 hour	Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000
Compression Set	2.0 % @Temperature 70.0 °C	2.0 % @Temperature 158 °F	ASTM D3584-95
	<= 10 % @Temperature 70.0 °C	<= 10 % @Temperature 158 °F	ASTM D3584-95
Seal Strength	9.40 g/25 mm	9.40 g/in	Release Adhesion, 180° Peel; ASTM D1000
	10.6 g/25 mm @Temperature 66.0 °C, Time 346000 sec	10.6 g/in @Temperature 151 °F, Time 96.0 hour	Release Adhesion, 180° Peel, 80% RH; ASTM D1000

Descriptive Properties
Tack	411 g		ASTM D2979 (1 second dwell), 96 hours at 66°C/80% RH
	424 g		ASTM D2979 (1 second dwell)
Tensile, CMD (lb) per ASTM D882	5		80% RH; 66°C; 96 hr
	9.1
Tensile, MD (lb) per ASTM D882	11.4		80% RH; 66°C; 96 hr
	12

關(guān)鍵詞:
供應(yīng)
聚氨酯TS
Rogers Corporation Poron? 4790-79SP-15012 Urethane Shock Pad Foam

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-37521.html

免責聲明: 本文 Rogers Corporation Poron? 4790-79SP-15012 Urethane Shock Pad Foam 僅代表作者個人觀點，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)