- 密度 [g/cm3]: 0.192
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.192 g/cc | 0.00694 lb/in3 | ASTM D3574-95 Test A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 78 % | 78 % | ASTM D882 | ||
| 74 % @Temperature 66.0 °C, Time 346000 sec | 74 % @Temperature 151 °F, Time 96.0 hour | 80% RH; ASTM D882 | |||
| Film Elongation at Break, TD | 32 % | 32 % | ASTM D882 | ||
| 66 % @Temperature 66.0 °C, Time 346000 sec | 66 % @Temperature 151 °F, Time 96.0 hour | 80% RH; ASTM D882 | |||
| Compressive Yield Strength | 0.0112 MPa @Strain 25.0 % | 1.63 psi @Strain 25.0 % | 0.2"/min. strain rate | ||
| Tear Strength | 0.310 kN/m @Time 1190 sec | 1.77 pli @Time 0.330 hour | Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000 | ||
| 0.320 kN/m @Time 1190 sec | 1.83 pli @Time 0.330 hour | Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000 | |||
| 0.320 kN/m @Time 259000 sec | 1.83 pli @Time 72.0 hour | Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000 | |||
| 0.330 kN/m @Time 1190 sec | 1.88 pli @Time 0.330 hour | Peel Adhesion, 180° Peel, to ABS; ASTM D1000 | |||
| 0.330 kN/m @Time 1190 sec | 1.88 pli @Time 0.330 hour | Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000 | |||
| 0.340 kN/m @Time 1190 sec | 1.94 pli @Time 0.330 hour | Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000 | |||
| 0.360 kN/m @Time 259000 sec | 2.05 pli @Time 72.0 hour | Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000 | |||
| 0.390 kN/m @Time 259000 sec | 2.23 pli @Time 72.0 hour | Peel Adhesion, 180° Peel, to ABS; ASTM D1000 | |||
| 0.390 kN/m @Time 259000 sec | 2.23 pli @Time 72.0 hour | Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000 | |||
| 0.404 kN/m @Time 259000 sec | 2.31 pli @Time 72.0 hour | Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000 | |||
| Compression Set | <= 5.0 % @Temperature 23.0 °C | <= 5.0 % @Temperature 73.4 °F | ASTM D3574-95 Test D | ||
| <= 10 % @Temperature 70.0 °C | <= 10 % @Temperature 158 °F | ASTM D3574-95 Test D | |||
| Seal Strength | 9.40 g/25 mm | 9.40 g/in | Release Adhesion, 180° Peel; ASTM D1000 | ||
| 10.6 g/25 mm @Temperature 66.0 °C, Time 346000 sec | 10.6 g/in @Temperature 151 °F, Time 96.0 hour | Release Adhesion, 180° Peel, 80% RH; ASTM D1000 | |||
| Descriptive Properties | |||||
| Tack | 411 g | ASTM D2979 (1 second dwell), 96 hours at 66°C/80% RH | |||
| 424 g | ASTM D2979 (1 second dwell) | ||||
| Tensile, CMD (lb) per ASTM D882 | 5 | 80% RH; 66°C; 96 hr | |||
| 9.1 | |||||
| Tensile, MD (lb) per ASTM D882 | 11.4 | 80% RH; 66°C; 96 hr | |||
| 12 | |||||