- 拉伸強度 [MPa]: 30.19
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 64 | >= 64 | |
| Tensile Strength, Yield | 30.19 MPa | 4379 psi | |
| Elongation at Yield | 567 % | 567 % | |
| 100% Modulus | 0.00260 GPa | 0.377 ksi | |
| 200% Modulus | 0.00570 GPa | 0.827 ksi | |
| 300% Modulus | 0.0100 GPa | 1.45 ksi | |
| Tear Strength | 34.8 kN/m | 199 pli | Die C |
| Compression Set | 32.4 % @Temperature 70.0 °C, Time 79200 sec | 32.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | |