- 拉伸強度 [MPa]: 22.6
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 | 88 | |
| Tensile Strength, Yield | 22.6 MPa | 3280 psi | |
| Elongation at Yield | 390 % | 390 % | |
| 100% Modulus | 0.007419 GPa | 1.076 ksi | |
| 200% Modulus | 0.01524 GPa | 2.211 ksi | |
| 300% Modulus | 0.02015 GPa | 2.923 ksi | |
| Tear Strength | 57.6 kN/m | 329 pli | |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 43.6 % @Temperature 70.0 °C, Time 79200 sec | 43.6 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |