- 拉伸強度 [MPa]: 13.14
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 25 | 25 | |
| Tensile Strength, Yield | 13.14 MPa | 1906 psi | |
| Elongation at Yield | 578 % | 578 % | |
| 100% Modulus | 0.000524 GPa | 0.0760 ksi | |
| 200% Modulus | 0.000841 GPa | 0.122 ksi | |
| 300% Modulus | 0.00125 GPa | 0.182 ksi | |
| Tear Strength | 16.5 kN/m | 94.1 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 149 °C | 0.250 hour @Temperature 300 °F | |