- 彎曲強度 [MPa]: 21.4
- 彎曲模量 [MPa]: 0.345
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 21.4 MPa | 3100 psi | ASTM D412 |
| Elongation at Break | 190 % | 190 % | ASTM D412 |
| Flexural Modulus | 0.345 GPa | 50.0 ksi | ASTM D790 |
| Tear Strength | 109 kN/m | 620 pli | ASTM D624 |
| Heat Distortion | 240 % | 240 % | 4" Heat sag - 250°F / 60 min (1/8" thickness); ASTM D3769 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 62.8 - 73.9 °C | 145 - 165 °F | |
| Injection Pressure | 9.65 - 17.2 MPa | 1400 - 2500 psi | |
| Gel Time | 0.0200 min | 0.0200 min | |