- 密度 [g/cm3]: 1.15
- 彎曲強(qiáng)度 [MPa]: 2.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.25 g/cc | 0.0415 - 0.0452 lb/in3 | |
| Viscosity | <= 260000 cP | <= 260000 cP | (Haake RU 20, 115 OSC, PK 2-1, 0; D= 1s-1) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 40 - 50 | 40 - 50 | DIN 53 505 |
| Tensile Strength, Ultimate | 2.30 - 2.90 MPa | 334 - 421 psi | DIN 54 504 |
| Elongation at Break | 450 % | 450 % | DIN 54 504 |
| Adhesive Bond Strength | 1.50 - 2.10 MPa | 218 - 305 psi | Lap Shear Strength (bond thickness: 2mm); EN 1465 |
| Tear Strength | 7.00 - 9.00 kN/m | 39.9 - 51.4 pli | ASTM D624 Form B |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | continuous (Cured condition) |
| 120 °C | 248 °F | short term (Cured condition) | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | continuous (Cured condition) |
| Shrinkage | 5.0 - 6.0 % | 5.0 - 6.0 % | after 14days at Room temp + 7 days at 70°C; DIN 52 451 |
| Processing Properties | Metric | English | Comments |
| Cure Time | 1440 min | 24.0 hour | 23°C / 50% RH |