- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.06
- 彎曲強度 [MPa]: 7.067
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | Cured | ||
| Water Absorption | 0.060 % | 0.060 % | 24 hours | ||
| Water Absorption at Saturation | 0.0015 % | 0.0015 % | 30 Days | ||
| Viscosity | 4500 cP @Temperature 25.0 °C | 4500 cP @Temperature 77.0 °F | |||
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 55 - 60 | 55 - 60 | |||
| Tensile Strength, Ultimate | 7.067 MPa | 1025 psi | |||
| Elongation at Break | 39 % | 39 % | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 6.80e+13 ohm-cm | <= 6.80e+13 ohm-cm | |||
| Surface Resistance | 3.50e+15 ohm | 3.50e+15 ohm | |||
| Dielectric Constant | 3.99 @Frequency 1000 Hz | 3.99 @Frequency 1000 Hz | |||
| Dielectric Strength | 23.0 kV/mm @Thickness 1.59 mm | 585 kV/in @Thickness 0.0625 in | |||
| Dissipation Factor | 0.053 @Frequency 1000 Hz | 0.053 @Frequency 1000 Hz | |||
| Arc Resistance | >= 120 sec | >= 120 sec | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 118 μm/m-°C @Temperature 20.0 °C | 65.6 μin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 0.649 W/m-K | 4.49 BTU-in/hr-ft2-°F | |||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | 100°C | ||
| 960 min | 16.0 hour | 80°C | |||
| 10080 min | 168.0 hour | 25°C | |||
| Pot Life | 12 - 15 min | 12 - 15 min | Value for 1 lbm at 25°C | ||
| Descriptive Properties | |||||
| Color | Blue | ||||