| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Solids Content | 60 % | 60 % | |
| Viscosity | 75 cP @Temperature 25.0 °C | 75 cP @Temperature 77.0 °F | Value represents initial mixed viscosity of components. |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.00e+12 ohm-cm | 6.00e+12 ohm-cm | Insulation Resistance; Recovery, 24 hrs after 10-day Cycling (25°C, 50% Relative Humidity) |
| 2.50e+13 ohm-cm | 2.50e+13 ohm-cm | Initial Insulation Resistance (50% Relative Humidity) | |
| 6.10e+10 ohm-cm @Temperature 65.0 °C | 6.10e+10 ohm-cm @Temperature 149 °F | Insulation Resistance During 10th day Cycling (95% Relative Humidity) | |
| Dielectric Constant | 3.42 | 3.42 | ASTM D150 |
| Dielectric Strength | 118 kV/mm | 3000 kV/in | ASTM D149 |
| Dissipation Factor | 0.016 @Frequency 1e+6 Hz | 0.016 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 54.4 °C | 130 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F | |
| Flash Point | 12.8 °C | 55.0 °F | (TCC) |
| Processing Properties | Metric | English | Comments |
| Cure Time | 180 min | 3.00 hour | 60°C |
| 240 - 300 min | 4.00 - 5.00 hour | Tack-free time at 25°C | |
| 10080 min | 168.0 hour | 25°C | |
| Pot Life | 240 - 360 min | 240 - 360 min | at 25°C |
| Shelf Life | 12.0 Month | 12.0 Month | Shelf Life Time at 25°C in original, unopened containers. |