- 密度 [g/cm3]: 1.61
- 吸水率 [%]: 0.11
- 彎曲強(qiáng)度 [MPa]: 8.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in3 | Cured | ||
| Water Absorption | 0.11 % | 0.11 % | 24 hours | ||
| Water Absorption at Saturation | 0.0042 % | 0.0042 % | 30 Days | ||
| Viscosity | 4750 cP @Temperature 25.0 °C | 4750 cP @Temperature 77.0 °F | |||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 45 - 55 | 45 - 55 | |||
| Tensile Strength, Ultimate | 8.62 MPa | 1250 psi | |||
| Elongation at Break | 50 % | 50 % | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1.70e+14 ohm-cm | <= 1.70e+14 ohm-cm | |||
| Surface Resistance | 8.90e+14 ohm | 8.90e+14 ohm | |||
| Dielectric Constant | 4.5 @Frequency 1000 Hz | 4.5 @Frequency 1000 Hz | |||
| Dielectric Strength | 25.6 kV/mm @Thickness 1.59 mm | 650 kV/in @Thickness 0.0625 in | |||
| Dissipation Factor | 0.075 @Frequency 1000 Hz | 0.075 @Frequency 1000 Hz | |||
| Arc Resistance | >= 120 sec | >= 120 sec | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 140 μm/m-°C @Temperature 20.0 °C | 77.8 μin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 0.305 W/m-K | 2.12 BTU-in/hr-ft2-°F | |||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 min | 4.00 hour | 100°C | ||
| 360 min | 6.00 hour | 60°C | |||
| 10080 min | 168.0 hour | 25°C | |||
| Pot Life | 30 - 35 min | 30 - 35 min | Value for 1 lbm at 25°C | ||
| Descriptive Properties | |||||
| Color | Tan or Black | ||||