- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.19
- 彎曲強度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | Cured | ||
| Water Absorption | 0.19 % | 0.19 % | 24 hours | ||
| Water Absorption at Saturation | 0.0048 % | 0.0048 % | 30 Days | ||
| Viscosity | 6000 cP @Temperature 25.0 °C | 6000 cP @Temperature 77.0 °F | |||
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 65 - 70 | 65 - 70 | |||
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | |||
| Elongation at Break | 35 - 40 % | 35 - 40 % | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1.60e+14 ohm-cm | <= 1.60e+14 ohm-cm | |||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |||
| Dielectric Constant | 4.3 @Frequency 1000 Hz | 4.3 @Frequency 1000 Hz | |||
| Dielectric Strength | 19.7 kV/mm @Thickness 1.59 mm | 500 kV/in @Thickness 0.0625 in | |||
| Dissipation Factor | 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | |||
| Arc Resistance | >= 120 sec | >= 120 sec | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 151 μm/m-°C @Temperature 20.0 °C | 83.9 μin/in-°F @Temperature 68.0 °F | |||
| Thermal Conductivity | 0.293 W/m-K | 2.03 BTU-in/hr-ft2-°F | |||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 240 min | 4.00 hour | 100°C | ||
| 360 min | 6.00 hour | 60°C | |||
| 10080 min | 168.0 hour | 25°C | |||
| Pot Life | 45 - 50 min | 45 - 50 min | Value for 1 lbm at 25°C | ||
| Descriptive Properties | |||||
| Color | Tan or Black | ||||