- 密度 [g/cm3]: 0.91
- 彎曲強(qiáng)度 [MPa]: 3.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in3 | A Component; ASTM D1475 |
| 1.23 g/cc | 0.0444 lb/in3 | B Component; ASTM D1475 | |
| Moisture Absorption at Equilibrium | 0.18 % | 0.18 % | Cured property; ASTM D570 |
| Viscosity | 50 cP | 50 cP | B Component; ASTM D1824 |
| 8000 cP | 8000 cP | A Component; ASTM D1824 | |
| Outgassing - Total Mass Loss | 0.38 % | 0.38 % | Cured property; at 10E-6 torr; ASTM E595 |
| Collected Volatile Condensable Material | 0.030 % | 0.030 % | Cured property; at 10E-6 torr; ASTM E595 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 50 - 60 | 50 - 60 | Cured property; ASTM D2240 |
| Tensile Strength, Ultimate | 3.31 MPa | 480 psi | Cured property; ASTM D412 |
| Elongation at Break | 325 % | 325 % | Cured property; ASTM D412 |
| Modulus of Elasticity | 0.00517 GPa | 0.750 ksi | Cured property; ASTM D412 |
| Adhesive Bond Strength | 3.62 MPa | 525 psi | Al-to-Al Lap Shear; Cured property; ASTM D1002 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.80e+15 ohm-cm | 8.80e+15 ohm-cm | Cured property; ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Dielectric Strength | 14.6 kV/mm @Thickness 12.7 mm | 370 kV/in @Thickness 0.500 in | Cured; ASTM D149 |
| >= 78.7 kV/mm @Thickness 0.127 mm | >= 2000 kV/in @Thickness 0.00500 in | Cured; ASTM D149 | |
| Dissipation Factor | 0.024 @Frequency 1000 Hz | 0.024 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 67.0 μm/m-°C @Temperature 20.0 °C | 37.2 μin/in-°F @Temperature 68.0 °F | Cured property; alpha 1 |
| 220 μm/m-°C @Temperature 20.0 °C | 122 μin/in-°F @Temperature 68.0 °F | Cured property; alpha 2 | |
| Thermal Conductivity | 0.176 W/m-K | 1.22 BTU-in/hr-ft2-°F | COLORA |
| Glass Transition Temp, Tg | -65.0 °C | -85.0 °F | Cured property; JMTP P200 |
| Flash Point | >= 150 °C | >= 302 °F | B Component; ASTM D92 |
| >= 200 °C | >= 392 °F | A Component; ASTM D92 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 °C | 176 °F | Cure 8 hrs. |
| 100 °C | 212 °F | Cure 4 hrs. | |