- 彎曲強度 [MPa]: 19.3
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Outgassing - Total Mass Loss | 0.187 % | 0.187 % | Cured property; at 10E-6 torr; ASTM E595 |
| Collected Volatile Condensable Material | 0.0020 % | 0.0020 % | Cured property; at 10E-6 torr; ASTM E595 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 88 | 88 | Cured property; ASTM D2240 |
| Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | Cured property; ASTM D412 |
| Elongation at Break | 525 % | 525 % | Cured property; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 μm/m-°C @Temperature 20.0 °C | 100 μin/in-°F @Temperature 68.0 °F | Cured property; alpha 1; JMTP P200 |
| Glass Transition Temp, Tg | -74.0 °C | -101 °F | Cured property; JMTP P200 |
| Flash Point | 10.0 °C | 50.0 °F | A Component; ASTM D92 |
| >= 150 °C | >= 302 °F | B Component; ASTM D92 | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 °C | 176 °F | Cure 8 hrs |
| 100 °C | 212 °F | Cure 5 hrs | |
| 125 °C | 257 °F | Cure 2 hrs | |