| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | |||
| Mooney Viscosity | 24 @Temperature 121 °C | 24 @Temperature 250 °F | ML1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 16.38 MPa | 2375 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| Elongation at Break | 180 % | 180 % | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| 100% Modulus | 0.007067 GPa | 1.025 ksi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| Compression Set | 14 % | 14 % | Aged 70 hours @ 200°C, O-rings -214; ASTM D395 Method B | ||
| Thermal Properties | Metric | English | Comments | ||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 | ||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 65.9 % | 65.9 % | |||
| Descriptive Properties | |||||
| Color | Opaque Off-White | ||||
| MH, Maximum Torque | 21 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 200°C, ASTM D5289 | |||
| 22 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | ||||
| ML, Minimum Torque | 0.7 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 200°C, ASTM D5289 | |||
| 0.8 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | ||||
| Solubility | Ketones and Esters | ||||
| t`50, Time to 50% cure | 0.6 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 200°C, ASTM D5289 | |||
| 1.6 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | ||||
| t`90 - Time to 90% cure | 0.8 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 200°C, ASTM D5289 | |||
| 2.3 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | ||||
| ts2 - Time to 2 in-lb rise from min | 0.5 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 200°C, ASTM D5289 | |||
| 1.4 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | ||||