| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | |||
| Mooney Viscosity | 28 @Temperature 121 °C | 28 @Temperature 250 °F | ML1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 74 | 74 | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240 | ||
| Tensile Strength at Break | 14.8 MPa | 2150 psi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| Elongation at Break | 890 % | 890 % | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D4645 | ||
| 100% Modulus | 0.0148 GPa | 2.15 ksi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C | ||
| Compression Set | 18 % | 18 % | Aged 70 hours @ 200°C | ||
| Thermal Properties | Metric | English | Comments | ||
| Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 | ||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 65.9 % | 65.9 % | |||
| Descriptive Properties | |||||
| 5`50, Time to 50% cure, minutes | 1.7 | 177°C | |||
| Color | Opaque Off-White | ||||
| MH, Maximum Torque, inch-lb @ 177°C | 23.8 | ||||
| ML, Minimum Torque inch-lb @ 177°C | 1.1 | ||||
| Solubility | Ketones and Esters | ||||
| t`90 - Time to 90% cure @ 177°C - minutes | 2.6 | ||||
| ts2 - Time to 2 in-lb rise from min @ 177°C - min | 1.4 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.