- 脆化溫度 [℃]: -35.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.98 g/cc | 1.98 g/cc | |||
| Mooney Viscosity | 60 @Temperature 121 °C | 60 @Temperature 250 °F | ML 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 75 | 75 | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D2240 | ||
| Tensile Strength at Break | 17.9 MPa | 2600 psi | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D412 | ||
| Elongation at Break | 165 % | 165 % | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D412 | ||
| 100% Modulus | 0.00110 GPa | 0.160 ksi | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D412 | ||
| Compression Set | 49 % @Treatment Temp. 200 °C, Time 252000 sec | 49 % @Treatment Temp. 392 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | ||
| 55 % @Treatment Temp. 200 °C, Time 605000 sec | 55 % @Treatment Temp. 392 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | |||
| 56 % @Treatment Temp. 230 °C, Time 252000 sec | 56 % @Treatment Temp. 446 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 25% Deformation; ASTM D395 | |||
| 68 % @Treatment Temp. 230 °C, Time 605000 sec | 68 % @Treatment Temp. 446 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 220 °C | 428 °F | |||
| Brittleness Temperature | -35.0 °C | -31.0 °F | |||
| Transformation Temperature | -2.00 °C | 28.4 °F | TR10 | ||
| Descriptive Properties | |||||
| Color | Off White to translucent | ||||
| Form | Slab | ||||
| MH, Maximum Toque | 13.4 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| ML, Minimum Torque | 2.0 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 0.6 Minute | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t'50, Time to 50% Cure | 0.8 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t'90, Time to 90% Cure | 1.5 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||