- 脆化溫度 [℃]: -35.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.00 g/cc | 2.00 g/cc | |||
| Mooney Viscosity | 100 @Temperature 121 °C | 100 @Temperature 250 °F | ML 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 81 | 81 | Press cure 15 Minutes @ 188°C, Post Cure 16 Hours @ 250°C | ||
| Tensile Strength at Break | 17.1 MPa | 2480 psi | Press cure 15 Minutes @ 188°C, Post Cure 16 Hours @ 250°C | ||
| Elongation at Break | 155 % | 155 % | Press cure 15 Minutes @ 188°C, Post Cure 16 Hours @ 250°C | ||
| 100% Modulus | 0.0121 GPa | 1.75 ksi | Press cure 15 Minutes @ 188°C, Post Cure 16 Hours @ 250°C | ||
| Compression Set | 17 % @Treatment Temp. 232 °C, Time 252000 sec | 17 % @Treatment Temp. 450 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 25% Deformation; ASTM D395 | ||
| 33 % @Treatment Temp. 232 °C, Time 605000 sec | 33 % @Treatment Temp. 450 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | |||
| 39 % @Treatment Temp. 300 °C, Time 252000 sec | 39 % @Treatment Temp. 572 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 18% Deformation; ASTM D395 | |||
| 46 % @Treatment Temp. 300 °C, Time 605000 sec | 46 % @Treatment Temp. 572 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 18% Deformation; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 315 °C | 599 °F | |||
| Brittleness Temperature | -35.0 °C | -31.0 °F | |||
| Transformation Temperature | -2.00 °C | 28.4 °F | TR10 | ||
| Descriptive Properties | |||||
| Color | Off-White | ||||
| Form | Slab | ||||
| MH, Maximum Toque | 17.6 inch-lb | 100 cpm, 0.5° Arc, 12 Minutes @ 188°C | |||
| ML, Minimum Torque | 0.95 inch-lb | 100 cpm, 0.5° Arc, 12 Minutes @ 188°C | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 1.7 Minute | 100 cpm, 0.5° Arc, 12 Minutes @ 188°C | |||
| t'50, Time to 50% Cure | 2.9 Minutes | 100 cpm, 0.5° Arc, 12 Minutes @ 188°C | |||
| t'90, Time to 90% Cure | 6.0 Minutes | 100 cpm, 0.5° Arc, 12 Minutes @ 188°C | |||