| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 g/cc | 1.80 g/cc | |||
| Mooney Viscosity | 100 @Temperature 150 °C | 100 @Temperature 302 °F | ML 1+10 | ||
| 150 @Temperature 121 °C | 150 @Temperature 250 °F | ML 1+10 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 77 | 77 | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D2240 | ||
| Tensile Strength at Break | 14.8 MPa | 2150 psi | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C | ||
| Elongation at Break | 175 % | 175 % | Ultimate, Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C | ||
| 100% Modulus | 0.00810 GPa | 1.17 ksi | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C | ||
| Compression Set | 14 % @Treatment Temp. 200 °C, Time 252000 sec | 14 % @Treatment Temp. 392 °F, Time 70.0 hour | Method B, -214 O-ring, 70 Hours; ASTM D395 | ||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 65.9 % | 65.9 % | |||
| Descriptive Properties | |||||
| Color | White to Off-White | ||||
| MH, Maximum Toque | 27.8 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| ML, Minimum Torque | 4.9 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| Solubility | Ketones and Esters | ||||
| t2, Time to 2 Inch-lb Rise from Minimum | 1.0 Minute | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t'50, Time to 50% Cure | 1.6 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||
| t'90, Time to 90% Cure | 2.3 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C | |||