- 彎曲強(qiáng)度 [MPa]: 9.4
- 脆化溫度 [℃]: -37.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 16 @Temperature 100 °C | 16 @Temperature 212 °F | ML 1+4. ?Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 63 | 63 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 9.40 MPa | 1360 psi | ASTM D412-80 |
| Elongation at Break | 260 % | 260 % | ASTM D412-80 |
| 100% Modulus | 0.00560 GPa | 0.812 ksi | ASTM D412-80 |
| Resilience | 67 | 67 | % Yerzley; ASTM D945-77 |
| Tear Strength Test | 180 | 180 | lb-in. Graves Die C; ASTM D642-54 |
| Abrasion | 70 | 70 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 60 % @Temperature 70.0 °C | 60 % @Temperature 158 °F | 22 hr at 70°C. Method B. ASTM D395-69 |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -37.0 °C | -34.6 °F | Brittleness Temperature |
| Brittleness Temperature | -37.0 °C | -34.6 °F | ASTM D746-79 |
| Clash Berg Stiffness Temperature | -24.0 °C | -11.2 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |