- 彎曲強度 [MPa]: 22.2
- 脆化溫度 [℃]: -14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 40 @Temperature 100 °C | 40 @Temperature 212 °F | ML 1+4. ?Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 77 | 77 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 22.2 MPa | 3220 psi | ASTM D412-80 |
| Elongation at Break | 210 % | 210 % | ASTM D412-80 |
| 100% Modulus | 0.0102 GPa | 1.48 ksi | ASTM D412-80 |
| Graves Tear Strength | 144 kN/m | 822 pli | Die C; ASTM D642-54 |
| Abrasion | 220 | 220 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 28 % @Temperature 70.0 °C | 28 % @Temperature 158 °F | 22 hr at 70°C original. Method B. ASTM D395-69. |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -14.0 °C | 6.80 °F | Brittleness Temperature |
| Brittleness Temperature | -14.0 °C | 6.80 °F | Wide variability between samples is observed.; ASTM D746 |
| Clash Berg Stiffness Temperature | -18.0 °C | -0.400 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |