- 彎曲強(qiáng)度 [MPa]: 19.8
- 脆化溫度 [℃]: -57.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 78 @Temperature 100 °C | 78 @Temperature 212 °F | ML 1+4. ?Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 65 | 65 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 19.8 MPa | 2870 psi | ASTM D412-80 |
| Elongation at Break | 320 % | 320 % | ASTM D412-80 |
| 100% Modulus | 0.00470 GPa | 0.682 ksi | ASTM D412-80 |
| Resilience | 72 | 72 | % Yerzley; ASTM D945-77 |
| Graves Tear Strength | 220 kN/m | 1260 pli | Die C; ASTM D642-54 |
| Abrasion | 270 | 270 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 11 % @Temperature 70.0 °C | 11 % @Temperature 158 °F | 22 hr at 70°C original. Method B. ASTM D395-69. |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -57.0 °C | -70.6 °F | Brittleness Temperature |
| Brittleness Temperature | -57.0 °C | -70.6 °F | Wide variability between samples is observed.; ASTM D746 |
| Clash Berg Stiffness Temperature | -26.0 °C | -14.8 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |