- 彎曲強度 [MPa]: 15.9
- 脆化溫度 [℃]: -40.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 120 @Temperature 100 °C | 120 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 63 | 63 | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Tensile Strength, Ultimate | 15.9 MPa | 2310 psi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Elongation at Break | 226 % | 226 % | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 50% Modulus | 0.00170 GPa | 0.247 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 100% Modulus | 0.00400 GPa | 0.580 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 200% Modulus | 0.0123 GPa | 1.78 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Tear Strength | 30.4 kN/m | 173 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 180°C |
| Compression Set | 7.0 % @Temperature 125 °C | 7.0 % @Temperature 257 °F | Pellets cured MDR t'95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -40.0 °C | -40.0 °F | Temperature Retraction, TR-10 |