- 密度 [g/cm3]: 1.083
- 彎曲強度 [MPa]: 18.8
- 脆化溫度 [℃]: -23.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.083 g/cc | 0.03913 lb/in3 | |
| Mooney Viscosity | 62 @Temperature 100 °C | 62 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 69 | 69 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 480 % | 480 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00390 GPa | 0.566 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00780 GPa | 1.13 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.0110 GPa | 1.60 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 39.3 kN/m | 224 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 61 % @Temperature 125 °C | 61 % @Temperature 257 °F | Pellets cured MDR t'95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -23.0 °C | -9.40 °F | Temperature Retraction, TR-10 |