- 密度 [g/cm3]: 1.185
- 彎曲強度 [MPa]: 10.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.185 g/cc | 0.04281 lb/in3 | |
| Mooney Viscosity | 47 @Temperature 100 °C | 47 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 10.4 MPa | 1510 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 446 % | 446 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00380 GPa | 0.551 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00750 GPa | 1.09 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00900 GPa | 1.31 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 88 % @Temperature 125 °C | 88 % @Temperature 257 °F | Pellets cured MDR t'95 + 15 min, 70 hr; Method B |