- 密度 [g/cm3]: 1.194
- 彎曲強度 [MPa]: 8.0
- 脆化溫度 [℃]: -21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.194 g/cc | 0.04314 lb/in3 | |
| Mooney Viscosity | 24 @Temperature 100 °C | 24 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 8.00 MPa | 1160 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 434 % | 434 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00310 GPa | 0.450 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00720 GPa | 1.04 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 35.9 kN/m | 205 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 95 % @Temperature 125 °C | 95 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -21.0 °C | -5.80 °F | Temperature Retraction, TR-10 |