- 密度 [g/cm3]: 1.362
- 彎曲強度 [MPa]: 11.1
- 脆化溫度 [℃]: -25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.362 g/cc | 0.04921 lb/in3 | |
| Mooney Viscosity | 70 @Temperature 100 °C | 70 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 82 | 82 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 11.1 MPa | 1610 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 393 % | 393 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00450 GPa | 0.653 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00690 GPa | 1.00 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00910 GPa | 1.32 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 30.7 kN/m | 175 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 93 % @Temperature 125 °C | 93 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -25.0 °C | -13.0 °F | Temperature Retraction, TR-10 |