| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D2240-91 |
| Tensile Strength, Ultimate | 14.8 MPa | 2150 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Elongation at Break | 290 % | 290 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| 100% Modulus | 0.00430 GPa | 0.624 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Tear Strength | 24.5 kN/m | 140 pli | Die C, Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 20 % @Temperature 200 °C | 20 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414-94 |