- 彎曲強度 [MPa]: 14.2
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 73 | 73 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D2240-91 |
| Tensile Strength, Ultimate | 14.2 MPa | 2060 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Elongation at Break | 200 % | 200 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| 100% Modulus | 0.00690 GPa | 1.00 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Tear Strength | 24.3 kN/m | 139 pli | Die C, Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 14 % @Temperature 200 °C | 14 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414-94 |