- 彎曲強度 [MPa]: 17.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 50 @Temperature 100 °C | 50 @Temperature 212 °F | ML(1+4) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 71 | 71 | |||
| Tensile Strength, Ultimate | 17.3 MPa | 2510 psi | |||
| Elongation at Break | 349 % | 349 % | |||
| 100% Modulus | 0.00510 GPa | 0.740 ksi | |||
| Tear Strength | 30.6 kN/m | 175 pli | ISO 34 | ||
| Compression Set | 26.8 % | 26.8 % | 70 hrs at 150°C | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | -27.2 °C | -17.0 °F | By DSC | ||
| Descriptive Properties | |||||
| DeMattia Dynamic Fatigue | Vamac? G failure cycles x 1.71 | ASTM D430, At 100°C, | |||
| Vamac? G failure cycles x 2.58 | ASTM D430, At 150°C | ||||
| Diak No. 1 | 1.5 parts | ||||
| DOTG Coaccelerator | 4 parts | ||||
| FEF Black(N550) | 50 parts | ||||
| Mooney Scorch at 121°C, t5 | 11.17 minutes | Time for 5 unit rise | |||
| Naugard? 445 antioxidant | 2 parts | ||||
| Stearic Acid | 1.5 parts | ||||
| Vamac? GXF | 100 parts | ||||
| Vanfre? VAM | 1 part | ||||
| Volume Swell | 0.267 | Immersed 70 hrs in IRM903 Oil at 150°C | |||