- 拉伸強度 [MPa]: 2.9
- 脆化溫度 [℃]: -26.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.89 g/cc | 1.89 g/cc | at 25°C |
| Mooney Viscosity | 35 @Temperature 121 °C | 35 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 72 | 72 | Peak value, at 25°C |
| Tensile Strength at Break | 12.8 MPa | 1860 psi | |
| Tensile Strength, Yield | 2.90 MPa @Strain 100 % | 421 psi @Strain 100 % | |
| Elongation at Break | 330 % | 330 % | |
| Tear Strength | 20.6 kN/m | 118 pli | at 25°C |
| Compression Set | 28 % | 28 % | 70 hours at 25°C |
| 17 % @Temperature 100 °C | 17 % @Temperature 212 °F | 70 hours | |
| 21 % @Temperature 175 °C | 21 % @Temperature 347 °F | 70 hours | |
| 29 % @Temperature 200 °C | 29 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -14.0 °C | 6.80 °F | TR test, TR10 |
| -13.6 °C | 7.52 °F | Gehman torsion test, T10 | |
| -7.00 °C | 19.4 °F | TR test, TR70 | |
| -4.00 °C | 24.8 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -26.0 °C | -14.8 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 6.30 min | 0.105 hour | Curelastmeter |