- 拉伸強度 [MPa]: 2.3
- 脆化溫度 [℃]: -26.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 3.00 g/cc | 3.00 g/cc | at 25°C |
| Mooney Viscosity | 40 @Temperature 121 °C | 40 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 67 | 67 | Peak value, at 25°C |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | |
| Tensile Strength, Yield | 2.30 MPa @Strain 100 % | 334 psi @Strain 100 % | |
| Elongation at Break | 320 % | 320 % | |
| Tear Strength | 19.6 kN/m | 112 pli | at 25°C |
| Compression Set | 13 % | 13 % | 70 hours at 25°C |
| 11 % @Temperature 100 °C | 11 % @Temperature 212 °F | 70 hours | |
| 15 % @Temperature 175 °C | 15 % @Temperature 347 °F | 70 hours | |
| 28 % @Temperature 200 °C | 28 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -14.0 °C | 6.80 °F | TR test, TR10 |
| -12.5 °C | 9.50 °F | Gehman torsion test, T10 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| -7.50 °C | 18.5 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -26.0 °C | -14.8 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 2.00 min | 0.0333 hour | Curelastmeter |