- 密度 [g/cm3]: 1.0
- 彎曲強(qiáng)度 [MPa]: 6.89
- 脆化溫度 [℃]: -51.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in3 | Base Elastomer |
| 1.15 - 1.35 g/cc | 0.0415 - 0.0488 lb/in3 | Compounded | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 30 - 95 | 30 - 95 | Depends on compounding |
| Tensile Strength, Ultimate | 6.89 - 24.1 MPa | 1000 - 3500 psi | Reinforced |
| 0.896 MPa @Temperature 204 °C | 130 psi @Temperature 400 °F | ||
| 4.83 MPa @Temperature 121 °C | 700 psi @Temperature 250 °F | ||
| Elongation at Break | 400 - 600 % | 400 - 600 % | Reinforced |
| 20 % @Temperature 204 °C | 20 % @Temperature 400 °F | ||
| 120 % @Temperature 121 °C | 120 % @Temperature 250 °F | ||
| 100% Modulus | 0.00300 GPa | 0.435 ksi | 200 mm/min |
| Compression Set | 5.0 % | 5.0 % | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 702 μm/m-°C @Temperature 20.0 °C | 390 μin/in-°F @Temperature 68.0 °F | |
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | |
| Brittleness Temperature | -51.1 °C | -60.0 °F | |
| Glass Transition Temp, Tg | -38.0 °C | -36.4 °F | Typical of rubber with 18% ACN content |
| -2.00 °C | 28.4 °F | Typical of rubber with 50% ACN content | |