- 密度 [g/cm3]: 0.7
- 吸水率 [%]: 0.1
- 拉伸強(qiáng)度 [MPa]: 3.82
- 彎曲強(qiáng)度 [MPa]: 0.0051
- 脆化溫度 [℃]: -73.0
- 透光率 [%]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.700 - 3.80 g/cc | 0.0253 - 0.137 lb/in3 | Average value: 1.32 g/cc Grade Count:856 |
| Solids Content | 75.0 - 100 % | 75.0 - 100 % | Average value: 97.8 % Grade Count:23 |
| Water Absorption | 0.100 - 3.00 % | 0.100 - 3.00 % | Average value: 1.60 % Grade Count:47 |
| Viscosity | 1.00 - 610000 cP | 1.00 - 610000 cP | Average value: 46500 cP Grade Count:86 |
| Thickness | 12.7 - 52400 microns | 0.500 - 2060 mil | Average value: 551 microns Grade Count:630 |
| Linear Mold Shrinkage | 0.00100 - 0.0350 cm/cm | 0.00100 - 0.0350 in/in | Average value: 0.0301 cm/cm Grade Count:122 |
| Outgassing - Total Mass Loss | 0.100 - 1.07 % | 0.100 - 1.07 % | Average value: 0.584 % Grade Count:7 |
| 0.100 - 0.340 % @Temperature 218 - 218 °C | 0.100 - 0.340 % @Temperature 425 - 425 °F | Average value: 0.220 % Grade Count:1 | |
| 0.100 - 0.340 % @Time 7200 - 7200 sec | 0.100 - 0.340 % @Time 2.00 - 2.00 hour | Average value: 0.220 % Grade Count:1 | |
| Storage Temperature | 0.000 - 40.0 °C | 32.0 - 104 °F | Average value: 20.0 °C Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 4.00 - 95.0 | 4.00 - 95.0 | Average value: 50.6 Grade Count:1089 |
| Hardness, Shore D | 14.5 - 95.2 | 14.5 - 95.2 | Average value: 53.6 Grade Count:12 |
| Hardness, Shore OO | 10.0 - 86.0 | 10.0 - 86.0 | Average value: 52.3 Grade Count:9 |
| Tensile Strength, Ultimate | 0.00510 - 165 MPa | 0.740 - 23900 psi | Average value: 6.93 MPa Grade Count:1094 |
| Tensile Strength, Yield | 3.82 - 145 MPa | 553 - 21000 psi | Average value: 12.3 MPa Grade Count:28 |
| Elongation at Break | 0.000 - 4460 % | 0.000 - 4460 % | Average value: 462 % Grade Count:1119 |
| Elongation at Yield | 0.000 - 38.0 % | 0.000 - 38.0 % | Average value: 27.5 % Grade Count:4 |
| Modulus of Elasticity | 0.0000448 - 1.72 GPa | 0.00650 - 250 ksi | Average value: 0.109 GPa Grade Count:85 |
| Compressive Modulus | 0.000200 - 0.00590 GPa | 0.0290 - 0.856 ksi | Average value: 0.00208 GPa Grade Count:10 |
| Poissons Ratio | 0.500 | 0.500 | Average value: 0.500 Grade Count:40 |
| Shear Modulus | 0.0000689 - 1.83 GPa | 0.0100 - 265 ksi | Average value: 0.208 GPa Grade Count:27 |
| Shear Strength | 0.965 - 6.05 MPa | 140 - 878 psi | Average value: 2.92 MPa Grade Count:35 |
| Adhesive Bond Strength | 0.0103 - 0.103 MPa | 1.50 - 15.0 psi | Average value: 0.0462 MPa Grade Count:44 |
| Penetration P(60), 1/10 mm | 36.0 - 135 | 36.0 - 135 | Average value: 70.0 Grade Count:3 |
| Tear Strength | 0.877 - 125 kN/m | 5.00 - 713 pli | Average value: 24.1 kN/m Grade Count:648 |
| 1.5777 - 2.2789 kN/m @Temperature 100 - 150 °C | 9.0024 - 13.003 pli @Temperature 212 - 302 °F | Average value: 1.93 kN/m Grade Count:1 | |
| Peel Strength | 0.0877 - 7.05 kN/m | 0.500 - 40.2 pli | Average value: 1.30 kN/m Grade Count:376 |
| Compression Set | 3.00 - 77.3 % | 3.00 - 77.3 % | Average value: 23.3 % Grade Count:167 |
| 4.50 - 45.0 % @Temperature 70.0 - 302 °C | 4.50 - 45.0 % @Temperature 158 - 576 °F | Average value: 28.9 % Grade Count:35 | |
| 4.50 - 45.0 % @Time 79200 - 259000 sec | 4.50 - 45.0 % @Time 22.0 - 72.0 hour | Average value: 28.9 % Grade Count:35 | |
| Tensile Set | 5.10 - 6.00 % | 5.10 - 6.00 % | Average value: 5.53 % Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.000103 - 9.00e+15 ohm-cm | 0.000103 - 9.00e+15 ohm-cm | Average value: 1.03e+15 ohm-cm Grade Count:63 |
| Shielding Effectiveness | 55.0 - 141 dB | 55.0 - 141 dB | Average value: 100 dB Grade Count:5 |
| Dielectric Constant | 2.20 - 7.07 | 2.20 - 7.07 | Average value: 4.30 Grade Count:51 |
| Dielectric Strength | 1.14 - 118 kV/mm | 29.0 - 3000 kV/in | Average value: 21.7 kV/mm Grade Count:547 |
| Dissipation Factor | 0.0000230 - 0.0700 | 0.0000230 - 0.0700 | Average value: 0.00782 Grade Count:47 |
| Arc Resistance | 180 - 193 sec | 180 - 193 sec | Average value: 189 sec Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.0 - 335 μm/m-°C | 6.11 - 186 μin/in-°F | Average value: 134 μm/m-°C Grade Count:43 |
| 1040 - 1040 μm/m-°C @Temperature 0.000 - 0.000 °C | 578 - 578 μin/in-°F @Temperature 32.0 - 32.0 °F | Average value: 1040 μm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 20.0 - 40.0 μm/m-°C | 11.1 - 22.2 μin/in-°F | Average value: 33.3 μm/m-°C Grade Count:3 |
| Specific Heat Capacity | 0.320 - 1.26 J/g-°C | 0.0765 - 0.301 BTU/lb-°F | Average value: 0.789 J/g-°C Grade Count:20 |
| 0.820 - 0.900 J/g-°C @Temperature 100 - 100 °C | 0.196 - 0.215 BTU/lb-°F @Temperature 212 - 212 °F | Average value: 0.837 J/g-°C Grade Count:15 | |
| Thermal Conductivity | 0.0600 - 6.50 W/m-K | 0.416 - 45.1 BTU-in/hr-ft2-°F | Average value: 1.09 W/m-K Grade Count:59 |
| 1.00 - 3.3867 W/m-K @Temperature 50.0 - 100 °C | 6.94 - 23.504 BTU-in/hr-ft2-°F @Temperature 122 - 212 °F | Average value: 2.08 W/m-K Grade Count:15 | |
| 1.50 - 4.69 W/m-K @Temperature 50.0 - 50.0 °C | 10.4 - 32.5 BTU-in/hr-ft2-°F @Temperature 122 - 122 °F | Average value: 2.08 W/m-K Grade Count:4 | |
| 1.50 - 4.69 W/m-K @Pressure 30.0 - 30.0 MPa | 10.4 - 32.5 BTU-in/hr-ft2-°F @Pressure 4350 - 4350 psi | Average value: 2.08 W/m-K Grade Count:4 | |
| Maximum Service Temperature, Air | 93.3 - 300 °C | 200 - 572 °F | Average value: 222 °C Grade Count:637 |
| Maximum Service Temperature, Inert | 154 - 260 °C | 310 - 500 °F | Average value: 221 °C Grade Count:59 |
| Minimum Service Temperature, Air | -136 - -40.0 °C | -212 - -40.0 °F | Average value: -58.1 °C Grade Count:667 |
| Brittleness Temperature | -73.0 - -65.0 °C | -99.4 - -85.0 °F | Average value: -70.3 °C Grade Count:3 |
| Glass Transition Temp, Tg | -120 - 118 °C | -184 - 244 °F | Average value: -106 °C Grade Count:37 |
| UL RTI, Electrical | 65.6 - 220 °C | 150 - 428 °F | Average value: 210 °C Grade Count:135 |
| UL RTI, Mechanical without Impact | 65.6 - 220 °C | 150 - 428 °F | Average value: 202 °C Grade Count:135 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:217 |
| HB - HB @Temperature 200 - 220 °C | HB - HB @Temperature 392 - 428 °F | Grade Count:15 | |
| Flammability Test | 0.000 - 25.0 | 0.000 - 25.0 | Average value: 8.00 Grade Count:49 |
| Flash Point | -4.00 - 100 °C | 24.8 - 212 °F | Average value: 33.0 °C Grade Count:4 |
| Shrinkage | 1.90 - 3.30 % | 1.90 - 3.30 % | Average value: 2.77 % Grade Count:7 |
| 0.300 - 0.500 % @Temperature 200 - 230 °C | 0.300 - 0.500 % @Temperature 392 - 446 °F | Average value: 0.433 % Grade Count:2 | |
| 0.300 - 0.500 % @Time 600 - 1800 sec | 0.300 - 0.500 % @Time 0.167 - 0.500 hour | Average value: 0.433 % Grade Count:2 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.39 - 1.41 | 1.39 - 1.41 | Average value: 1.40 Grade Count:5 |
| Transmission, Visible | 20.0 - 90.0 % | 20.0 - 90.0 % | Average value: 47.3 % Grade Count:173 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 165 °C | 302 - 329 °F | Average value: 153 °C Grade Count:6 |
| Nozzle Temperature | 20.0 °C | 68.0 °F | Average value: 20.0 °C Grade Count:111 |
| Mold Temperature | 140 - 230 °C | 284 - 446 °F | Average value: 185 °C Grade Count:111 |
| Injection Pressure | 5.00 - 15.0 MPa | 725 - 2180 psi | Average value: 10.0 MPa Grade Count:111 |
| Hold Pressure | 5.00 MPa | 725 psi | Average value: 5.00 MPa Grade Count:111 |
| Extrusion Rate | 3.75 - 200 g/min | 3.75 - 200 g/min | Average value: 91.8 g/min Grade Count:30 |
| Cure Time | 3.00 - 10100 min | 0.0500 - 168 hour | Average value: 1500 min Grade Count:99 |
| 1.60 - 1020 min @Temperature 50.0 - 249 °C | 0.0267 - 17.0 hour @Temperature 122 - 480 °F | Average value: 51.3 min Grade Count:532 | |
| 5.00 - 15.0 min @Temperature 110 - 177 °C | 0.0833 - 0.250 hour @Temperature 230 - 350 °F | Average value: 51.3 min Grade Count:350 | |
| 5.00 - 15.0 min @Pressure 0.0689 - 3.45 MPa | 0.0833 - 0.250 hour @Pressure 10.0 - 500 psi | Average value: 51.3 min Grade Count:350 | |
| Pot Life | 10.0 - 4320 min | 10.0 - 4320 min | Average value: 2370 min Grade Count:40 |
| Shelf Life | 3.00 - 60.0 Month | 3.00 - 60.0 Month | Average value: 12.2 Month Grade Count:628 |
| 3.00 - 60.0 Month @Temperature -15.0 - 27.0 °C | 3.00 - 60.0 Month @Temperature 5.00 - 80.6 °F | Average value: 9.67 Month Grade Count:85 | |
- 關(guān)鍵詞:
- TSE
- 供應(yīng)
- Overview of materials for Silicone Rubber