- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.45
- 斷裂伸長率 [%]: 76.0
- 彎曲強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.600 g/cc | 0.0217 lb/in3 | ASTM D1895 |
| Water Absorption | 0.45 % | 0.45 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Yield Strength | 228 MPa | 33100 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.8 | 5.8 | 60 Hz; ASTM D150 |
| 5.8 | 5.8 | 60 Hz; ASTM D150 | |
| Dielectric Strength | 14.2 kV/mm | 361 kV/in | ASTM D149 |
| Dissipation Factor | 0.030 | 0.030 | 1 MHz; ASTM D150 |
| 0.060 | 0.060 | 60 Hz; ASTM D150 | |
| Comparative Tracking Index | 140 V | 140 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.47 mm | 302 °F @Thickness 0.0579 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.47 mm | 302 °F @Thickness 0.0579 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.47 mm | 302 °F @Thickness 0.0579 in | |
| Flammability, UL94 | HB | HB | 3.05mm |
| HB | HB | 3.05mm | |