- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.18
- 斷裂伸長率 [%]: 69.0
- 彎曲強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 9.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.650 g/cc | 0.0235 lb/in3 | ASTM D1895 |
| Water Absorption | 0.18 % | 0.18 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Compressive Yield Strength | 206 MPa | 29900 psi | ASTM D695 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.8 | 4.8 | 1MHz; ASTM D150 |
| 8.0 | 8.0 | 60 Hz; ASTM D150 | |
| Dielectric Strength | 14.8 kV/mm | 376 kV/in | ASTM D149 |
| Dissipation Factor | 0.040 | 0.040 | 1 MHz; ASTM D150 |
| 0.15 | 0.15 | 60 Hz; ASTM D150 | |
| Comparative Tracking Index | 185 V | 185 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| Flammability, UL94 | V-0 | V-0 | 1.57 mm |
| V-0 | V-0 | 1.57 mm | |
| Oxygen Index | 31.4 % | 31.4 % | ASTM D2863 |