- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 0.109
- 缺口沖擊強(qiáng)度: 0.14
- 彎曲強(qiáng)度 [MPa]: 46.0
- 彎曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in3 | ASTM D1895 |
| Density | 1.56 g/cc | 0.0564 lb/in3 | ASTM D792 |
| Water Absorption | 0.109 % | 0.109 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00251 cm/cm | 0.00251 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 89 | 89 | ASTM D785 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 0.50 % | 0.50 % | ASTM D638 |
| Tensile Modulus | 9.80 GPa | 1420 ksi | ASTM D638 |
| Flexural Strength | 67.0 MPa | 9720 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Compressive Strength | 195 MPa | 28300 psi | ASTM D695 |
| Izod Impact, Notched | 0.140 J/cm | 0.262 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.187 J/cm2 | 0.890 ft-lb/in2 | ASTM D256 |
| Impact | 78 | 78 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.60e+11 ohm-cm | 7.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.9 | 5.9 | ASTM D150 |
| Dielectric Strength | 11.6 kV/mm | 295 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.051 | 0.051 | ASTM D150 |
| Arc Resistance | 177 sec | 177 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C @Temperature 40.0 - 130 °C | 22.2 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.510 W/m-K @Temperature 100 °C | 3.54 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 232 °C | 450 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 45 % | 45 % | ASTM D2863 |
| Shrinkage | 0.143 % | 0.143 % | 72 hr, 120oC; ASTM D1299 |