- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 0.099
- 缺口沖擊強度: 0.144
- 彎曲強度 [MPa]: 49.0
- 彎曲模量 [MPa]: 8.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.630 g/cc | 0.0228 lb/in3 | ASTM D1895 |
| Density | 1.56 g/cc | 0.0564 lb/in3 | ASTM D792 |
| Water Absorption | 0.099 % | 0.099 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0066 cm/cm | 0.0066 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 84 | 84 | ASTM D785 |
| Tensile Strength, Ultimate | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 0.65 % | 0.65 % | ASTM D638 |
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 8.60 GPa | 1250 ksi | ASTM D790 |
| Compressive Strength | 186 MPa | 27000 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 3.53 GPa | 512 ksi | Calculated |
| Izod Impact, Notched | 0.144 J/cm | 0.270 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.158 J/cm2 | 0.752 ft-lb/in2 | ASTM D256 |
| Impact | 74 | 74 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.60e+11 ohm-cm | 6.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.6 | 5.6 | ASTM D150 |
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.053 | 0.053 | ASTM D150 |
| Arc Resistance | 166 sec | 166 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 μm/m-°C @Temperature 40.0 - 130 °C | 20.0 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.470 W/m-K @Temperature 100 °C | 3.26 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 216 °C | 421 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |
| Oxygen Index | 34 % | 34 % | ASTM D2863 |
| Shrinkage | 0.163 % | 0.163 % | 72 hr, 120oC; ASTM D1299 |