- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.286
- 缺口沖擊強(qiáng)度: 0.159
- 彎曲強(qiáng)度 [MPa]: 62.0
- 彎曲模量 [MPa]: 9.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.720 g/cc | 0.0260 lb/in3 | ASTM D1895 |
| Density | 1.65 g/cc | 0.0596 lb/in3 | ASTM D792 |
| Water Absorption | 0.286 % | 0.286 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0068 cm/cm | 0.0068 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 71 | 71 | ASTM D785 |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | 0.70 % | 0.70 % | ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | ASTM D790 |
| Compressive Strength | 151 MPa | 21900 psi | ASTM D695 |
| Poissons Ratio | 0.31 | 0.31 | ASTM D638 |
| Shear Modulus | 4.20 GPa | 609 ksi | Calculated |
| Izod Impact, Notched | 0.159 J/cm | 0.298 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.165 J/cm2 | 0.785 ft-lb/in2 | ASTM D256 |
| Impact | 85 | 85 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.70e+12 ohm-cm | 3.70e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.9 | 6.9 | ASTM D150 |
| Dielectric Strength | 6.30 kV/mm | 160 kV/in | Step by Step; ASTM D149 |
| 9.50 kV/mm | 241 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.069 | 0.069 | ASTM D150 |
| Arc Resistance | 186 sec | 186 sec | ASTM D495 |
| Comparative Tracking Index | 575 V | 575 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 52.0 μm/m-°C @Temperature 40.0 - 130 °C | 28.9 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 142 °C | 288 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Shrinkage | 0.90 % | 0.90 % | 240 hr, 105oC; ASTM D1299 |