- 拉伸強度 [MPa]: 64.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.25 - 1.35 g/cc @Thickness 1.57 mm | 1.25 - 1.35 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.3 % @Thickness 1.57 mm | 1.3 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 110 - 130 @Thickness 1.57 mm | 110 - 130 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 64.1 MPa @Thickness 1.57 mm | 9300 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 75.8 MPa @Thickness 1.57 mm | 11000 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Modulus of Elasticity | 4.14 GPa @Thickness 1.57 mm | 600 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 6.21 GPa @Thickness 1.57 mm | 900 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 131 MPa @Thickness 1.57 mm | 19000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 200 MPa @Thickness 1.57 mm | 29000 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 310 MPa @Thickness 12.7 mm | 45000 psi @Thickness 0.500 in | ASTM D695 | ||
| Shear Strength | 100 MPa @Thickness 15.7 mm | 14500 psi @Thickness 0.620 in | ASTM D732 | ||
| Izod Impact, Unnotched | 2.83 J/cm @Thickness 12.7 mm | 5.30 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 3.31 J/cm @Thickness 12.7 mm | 6.20 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.8 @Thickness 1.57 mm | 3.8 @Thickness 0.0620 in | Permittivity, Cond D-24/23; ASTM D150 | ||
| Dielectric Strength | 21.7 kV/mm @Thickness 1.57 mm | 550 kV/in @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S.T. | ||
| 27.6 kV/mm @Thickness 1.57 mm | 700 kV/in @Thickness 0.0620 in | Cond A; ASTM D229 S.T. | |||
| Dielectric Breakdown | 35000 V @Thickness 1.57 mm | 35000 V @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S/S | ||
| 65000 V @Thickness 1.57 mm | 65000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | |||
| Dissipation Factor | 0.035 @Thickness 1.57 mm | 0.035 @Thickness 0.0620 in | Cond D-24/23; ASTM D150 | ||
| Arc Resistance | 200 sec @Thickness 3.17 mm | 200 sec @Thickness 0.125 in | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 μm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 22.2 μin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 45.0 μm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 25.0 μin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 2400 lb | 0.5", ASTM D229 | |||
| Color | Natural | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.