- 密度 [g/cm3]: 1.51
- 彎曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in3 | ISO 1183 | ||
| Apparent Bulk Density | 0.680 g/cc | 0.0246 lb/in3 | ISO 60 | ||
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | Compression molding; ISO 2577 | ||
| 0.0075 cm/cm | 0.0075 in/in | Injection molding; ISO 2577 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 275 MPa | 39900 psi | H 961/30; ISO 2039/P1 | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 - 1/2 | ||
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 - 1/2 | ||
| Flexural Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 | ||
| Compressive Strength | 165 MPa | 23900 psi | Test specimen flat tested; ISO 604 | ||
| Charpy Impact Unnotched | 0.650 J/cm2 @Temperature 23.0 °C | 3.09 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1/2 eU | ||
| Charpy Impact, Notched | 0.140 J/cm2 @Temperature 23.0 °C | 0.666 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1/2 eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 13 @Frequency 100 Hz | 13 @Frequency 100 Hz | IEC 60250 | ||
| Dielectric Strength | 15.0 kV/mm @Thickness 1.00 mm | 381 kV/in @Thickness 0.0394 in | IEC 60243-P1 | ||
| Dissipation Factor | 0.30 @Frequency 100 Hz | 0.30 @Frequency 100 Hz | IEC 60250 | ||
| Arc Resistance | 120 - 180 sec @Thickness 3.00 mm | 120 - 180 sec @Thickness 0.118 in | BN, BK | ||
| Comparative Tracking Index | 175 - 250 V @Thickness 3.00 mm | 175 - 250 V @Thickness 0.118 in | BN, BK | ||
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 1.50 mm | 60 - 120 sec @Thickness 0.0591 in | BN, BK | ||
| >= 120 sec @Thickness 3.00 mm | >= 120 sec @Thickness 0.118 in | BN, BK | |||
| High Amp Arc Ignition, HAI | 30 - 60 arcs @Thickness 1.50 mm | 30 - 60 arcs @Thickness 0.0591 in | BN, BK | ||
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min @Thickness 3.00 mm | 0.394 - 1.00 in/min @Thickness 0.118 in | BN, BK | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 8.0 MPa | 115 °C | 239 °F | ISO 75-2 | ||
| UL RTI, Electrical | 150 °C @Thickness 1.50 mm | 302 °F @Thickness 0.0591 in | BN, BK | ||
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.50 mm | 302 °F @Thickness 0.0591 in | BN, BK | ||
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.50 mm | 302 °F @Thickness 0.0591 in | BN, BK | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | BN, BK | ||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | BN, BK | |||
| Shrinkage | 0.35 % | 0.35 % | Injection molding, 168 hours/110°C; ISO 2577 | ||
| 0.55 % | 0.55 % | Compression molding, 168 hours/110°C; ISO 2577 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 60.0 - 75.0 °C | 140 - 167 °F | Injection molding | ||
| Nozzle Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection molding | ||
| Melt Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection molding | ||
| Mold Temperature | 160 - 190 °C | 320 - 374 °F | Compression molding | ||
| 160 - 190 °C | 320 - 374 °F | Injection molding | |||
| Injection Pressure | >= 15.0 MPa | >= 2180 psi | Compression and injection cavity mold pressure | ||
| Back Pressure | 0.500 - 2.00 MPa | 72.5 - 290 psi | Injection molding | ||
| Cure Time | 0.167 - 0.333 min | 0.00278 - 0.00556 hour | Per 1 mm of wall thickness, injection molding | ||
| 0.333 - 0.667 min | 0.00556 - 0.0111 hour | Per 1 mm of wall thickness, compression molding | |||
| Descriptive Properties | |||||
| Chromatic Spectrum | All Colors | ||||
| Creep Rupture Strength | Very Good | ||||
| Holding Pressure | Approximately 40-60% of injection pressure | ||||
| Media Resistance | Very Good | ||||
| Moisture Absorption | 50 mg | ISO 62, 24 hours at 23°C | |||
| Reserves by Peak Temperature | Very High | ||||
| Thermal Expansion | Very Slight | ||||