- 密度 [g/cm3]: 1.43
- 彎曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ISO 1183 | ||
| Apparent Bulk Density | 0.600 g/cc | 0.0217 lb/in3 | ISO 60 | ||
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | Compression molding; ISO 2577 | ||
| 0.0065 cm/cm | 0.0065 in/in | Injection molding; ISO 2577 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 275 MPa | 39900 psi | H 961/30; ISO 2039/P1 | ||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 - 1/2 | ||
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 - 1/2 | ||
| Flexural Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 | ||
| Compressive Strength | 250 MPa | 36300 psi | Test specimen flat tested; ISO 604 | ||
| Charpy Impact Unnotched | 0.650 J/cm2 @Temperature 23.0 °C | 3.09 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1/2 eU | ||
| Charpy Impact, Notched | 0.150 J/cm2 @Temperature 23.0 °C | 0.714 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1/2 eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 14 @Frequency 100 Hz | 14 @Frequency 100 Hz | IEC 60250 | ||
| Dielectric Strength | 15.0 kV/mm @Thickness 1.00 mm | 381 kV/in @Thickness 0.0394 in | IEC 60243-P1 | ||
| Dissipation Factor | 0.22 @Frequency 100 Hz | 0.22 @Frequency 100 Hz | IEC 60250 | ||
| Comparative Tracking Index | 125 V | 125 V | Test liquid A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 8.0 MPa | 105 °C | 221 °F | ISO 75-2 | ||
| Shrinkage | 0.35 % | 0.35 % | Compression molding, 168 hours/110°C; ISO 2577 | ||
| 0.55 % | 0.55 % | Injection molding, 168 hours/110°C; ISO 2577 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 60.0 - 75.0 °C | 140 - 167 °F | Injection molding | ||
| Nozzle Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection molding | ||
| Melt Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection molding | ||
| Mold Temperature | 160 - 190 °C | 320 - 374 °F | Injection molding | ||
| 160 - 190 °C | 320 - 374 °F | Compression molding | |||
| Injection Pressure | >= 15.0 MPa | >= 2180 psi | Compression and injection cavity mold pressure | ||
| Back Pressure | 0.500 - 2.00 MPa | 72.5 - 290 psi | Injection molding | ||
| Cure Time | 0.167 - 0.333 min | 0.00278 - 0.00556 hour | Per 1 mm of wall thickness, injection molding | ||
| 0.333 - 0.667 min | 0.00556 - 0.0111 hour | Per 1 mm of wall thickness, compression molding | |||
| Descriptive Properties | |||||
| Chromatic Spectrum | Subdued Colors | ||||
| Creep Rupture Strength | Good | ||||
| Holding Pressure | Approximately 40-60% of injection pressure | ||||
| Media Resistance | Good | ||||
| Moisture Absorption | 110 mg | ISO 62, 24 hours at 23°C | |||
| Reserves by Peak Temperature | High | ||||
| Thermal Expansion | Slight | ||||