Momentive Performance Materials PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures,

Momentive Performance Materials PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures, 物性表: Momentive Performance Materials PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures,物性表及特性介紹,Momentive Performance Materials PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures,注塑參數(shù)詳情,如需Momentive Performance Materials PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures,下載, 可到相關(guān)下載區(qū)下載

密度 [g/cm3]: 1.69
彎曲模量 [MPa]: 12.0

Physical Properties	Metric	English	Comments

Density	1.69 g/cc	0.0611 lb/in3	ISO 1183
Apparent Bulk Density	0.710 g/cc	0.0257 lb/in3	ISO 60
Linear Mold Shrinkage, Flow	0.00070 cm/cm	0.00070 in/in	Compression molding; ISO 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	425 MPa	61600 psi	H 961/30; ISO 2039/P1
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527 - 1/2
Tensile Modulus	13.5 GPa	1960 ksi	1 mm/min; ISO 527 - 1/2
Flexural Strength	150 MPa	21800 psi	2 mm/min; ISO 178
Flexural Modulus	12.0 GPa	1740 ksi	ISO 178
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Charpy Impact Unnotched	1.10 J/cm2 @Temperature 23.0 °C	5.24 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1/2 eU
Charpy Impact, Notched	0.350 J/cm2 @Temperature 23.0 °C	1.67 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1/2 eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Surface Resistance	1.00e+11 ohm	1.00e+11 ohm	IEC 60093
Dielectric Constant	6.0 @Frequency 100 Hz	6.0 @Frequency 100 Hz	IEC 60250
Dielectric Strength	35.0 kV/mm @Thickness 1.00 mm	889 kV/in @Thickness 0.0394 in	IEC 60243-P1
Dissipation Factor	0.060 @Frequency 100 Hz	0.060 @Frequency 100 Hz	IEC 60250

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	175 °C	347 °F	ISO 75-2
Shrinkage	0.070 %	0.070 %	Compression molding, 168 hours/110°C; ISO 2577

Processing Properties	Metric	English	Comments
Feed Temperature	60.0 - 75.0 °C	140 - 167 °F	Injection molding
Nozzle Temperature	80.0 - 100 °C	176 - 212 °F	Injection molding
Melt Temperature	80.0 - 100 °C	176 - 212 °F	Injection molding
Mold Temperature	160 - 190 °C	320 - 374 °F	Injection molding
	160 - 190 °C	320 - 374 °F	Compression molding
Injection Pressure	>= 15.0 MPa	>= 2180 psi	Compression and injection cavity mold pressure
Back Pressure	0.500 - 2.00 MPa	72.5 - 290 psi	Injection molding
Cure Time	0.167 - 0.333 min	0.00278 - 0.00556 hour	Per 1 mm of wall thickness, injection molding
	0.333 - 0.667 min	0.00556 - 0.0111 hour	Per 1 mm of wall thickness, compression molding

Descriptive Properties
Chromatic Spectrum	All Colors
Creep Rupture Strength	Very Good
Holding Pressure	Approximately 40-60% of injection pressure
Media Resistance	Very Good
Moisture Absorption	11 mg		ISO 62, 24 hours at 23°C
Reserves by Peak Temperature	Very High
Thermal Expansion	Very Slight

關(guān)鍵詞:
供應(yīng)
酚醛樹(shù)脂
Resistant to High Temperatures
Momentive Performance Materials PF 4260 Phenolic Formaldehyde Resin

轉(zhuǎn)載請(qǐng)注明: 轉(zhuǎn)自中國(guó)塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-34870.html

免責(zé)聲明: 本文 Momentive Performance Materials PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures, 僅代表作者個(gè)人觀點(diǎn)，中國(guó)塑膠原料之家無(wú)關(guān)。中國(guó)塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問(wèn)題需要處理，請(qǐng)與我們聯(lián)絡(luò)