Momentive Performance Materials PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwashe

Momentive Performance Materials PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwashe 物性表: Momentive Performance Materials PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwashe物性表及特性介紹,Momentive Performance Materials PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwashe注塑參數(shù)詳情,如需Momentive Performance Materials PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwashe下載, 可到相關(guān)下載區(qū)下載

密度 [g/cm3]: 1.47
彎曲模量 [MPa]: 7.50

Physical Properties	Metric	English	Comments

Density	1.47 g/cc	0.0531 lb/in3	ISO 1183
Apparent Bulk Density	0.650 g/cc	0.0235 lb/in3	ISO 60
Linear Mold Shrinkage, Flow	0.0035 cm/cm	0.0035 in/in	Compression molding; ISO 2577
	0.0075 cm/cm	0.0075 in/in	Injection molding; ISO 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	350 MPa	50800 psi	H 961/30; ISO 2039/P1
Tensile Strength at Break	55.0 MPa	7980 psi	5 mm/min; ISO 527 - 1/2
Tensile Modulus	7.50 GPa	1090 ksi	1 mm/min; ISO 527 - 1/2
Flexural Strength	95.0 MPa	13800 psi	2 mm/min; ISO 178
Flexural Modulus	7.50 GPa	1090 ksi	ISO 178
Compressive Strength	250 MPa	36300 psi	Test specimen flat tested; ISO 604
Charpy Impact Unnotched	0.700 J/cm2 @Temperature 23.0 °C	3.33 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1/2 eU
Charpy Impact, Notched	0.140 J/cm2 @Temperature 23.0 °C	0.666 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1/2 eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 ohm-cm	1.00e+11 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Constant	9.0 @Frequency 100 Hz	9.0 @Frequency 100 Hz	IEC 60250
Dielectric Strength	25.0 kV/mm @Thickness 1.00 mm	635 kV/in @Thickness 0.0394 in	IEC 60243-P1
Dissipation Factor	0.25 @Frequency 100 Hz	0.25 @Frequency 100 Hz	IEC 60250
Arc Resistance	125 - 130 sec	125 - 130 sec	ASTM D495
Comparative Tracking Index	125 V	125 V	Test liquid A; IEC 60112
Hot Wire Ignition, HWI	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	(ALL)
High Amp Arc Ignition, HAI	60 - 120 arcs @Thickness 1.50 mm	60 - 120 arcs @Thickness 0.0591 in	(ALL)
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	ALL
High Voltage Arc-Tracking Rate, HVTR	10.0 - 25.4 mm/min @Thickness 3.00 mm	0.394 - 1.00 in/min @Thickness 0.118 in	ALL

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	145 °C	293 °F	<20000 hours; IEC 60216-P1
	230 °C	446 °F	< 50 hours; IEC 60216-P1
Deflection Temperature at 8.0 MPa	125 °C	257 °F	ISO 75-2
UL RTI, Electrical	150 °C @Thickness 1.50 mm	302 °F @Thickness 0.0591 in	(ALL)
UL RTI, Mechanical with Impact	150 °C @Thickness 1.50 mm	302 °F @Thickness 0.0591 in	(ALL)
UL RTI, Mechanical without Impact	150 °C @Thickness 1.50 mm	302 °F @Thickness 0.0591 in	(ALL)
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	(ALL)
Shrinkage	0.45 %	0.45 %	Injection molding, 168 hours/110°C; ISO 2577
	0.45 %	0.45 %	Compression molding, 168 hours/110°C; ISO 2577

Processing Properties	Metric	English	Comments
Feed Temperature	60.0 - 75.0 °C	140 - 167 °F	Injection molding
Nozzle Temperature	80.0 - 100 °C	176 - 212 °F	Injection molding
Melt Temperature	80.0 - 100 °C	176 - 212 °F	Injection molding
Mold Temperature	160 - 190 °C	320 - 374 °F	Injection molding
	160 - 190 °C	320 - 374 °F	Compression molding
Injection Pressure	>= 15.0 MPa	>= 2180 psi	Compression and injection cavity mold pressure
Back Pressure	0.500 - 2.00 MPa	72.5 - 290 psi	Injection molding
Cure Time	0.167 - 0.333 min	0.00278 - 0.00556 hour	Per 1 mm of wall thickness, injection molding
	0.333 - 0.667 min	0.00556 - 0.0111 hour	Per 1 mm of wall thickness, compression molding

Descriptive Properties
Chromatic Spectrum	All Colors
Creep Rupture Strength	Very Good
Holding Pressure	Approximately 40-60% of injection pressure
Media Resistance	Very Good
Moisture Absorption	50 mg		ISO 62, 24 hours at 23°C
Reserves by Peak Temperature	Very High
Thermal Expansion	Very Slight

關(guān)鍵詞:
供應(yīng)
酚醛樹脂
High Surface Quality
Dishwashe
Momentive Performance Materials PF 2400 Phenolic Formaldehyde Resin

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-34869.html

免責(zé)聲明: 本文 Momentive Performance Materials PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwashe 僅代表作者個人觀點，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)