- 密度 [g/cm3]: 1.88
- 吸水率 [%]: 0.07
- 缺口沖擊強度: 0.29
- 彎曲強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 17.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.975 g/cc | 0.0352 lb/in3 | Powder; ASTM D1895 | ||
| Density | 1.88 g/cc | 0.0679 lb/in3 | ASTM D-792 | ||
| Water Absorption | 0.070 % | 0.070 % | 24 hour; ASTM D570 | ||
| 0.15 % | 0.15 % | 48 hour; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0023 cm/cm | 0.0023 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 123 | 123 | ASTM D785 | ||
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ASTM D638 | ||
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 | ||
| Flexural Modulus | 17.1 GPa | 2480 ksi | ASTM D790 | ||
| Compressive Strength | 230 MPa | 33400 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.6 @Frequency 1e+6 Hz | 4.6 @Frequency 1e+6 Hz | Wet; ASTM D150 | ||
| Dielectric Strength | 14.4 kV/mm | 366 kV/in | 60 Hz, wet, SS; ASTM D149 | ||
| 16.1 kV/mm | 409 kV/in | ST; ASTM D149 | |||
| Dissipation Factor | 0.012 @Frequency 1e+6 Hz | 0.012 @Frequency 1e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 180 sec | 180 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 μm/m-°C @Temperature 20.0 °C | 10.6 μin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Available Molding Grades | Compression, Transfer, Injection | ||||
| Color | Black, Green | ||||
| Form | Granular | ||||