- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.35
- 彎曲模量 [MPa]: 8.30
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 g/cc | 0.0181 lb/in3 | ASTM D1895 | ||
| Density | 1.39 g/cc | 0.0502 lb/in3 | ASTM D792 | ||
| Water Absorption | 0.30 % @Time 86400 sec | 0.30 % @Time 24.0 hour | ASTM D570 | ||
| 1.7 % @Time 173000 sec | 1.7 % @Time 48.0 hour | ASTM D570 | |||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 75 | 75 | ASTM D785 | ||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 | ||
| Flexural Strength | 69.0 MPa | 10000 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 8.30 GPa | 1200 ksi | ASTM D790 | ||
| Compressive Strength | 169 MPa | 24500 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 1.00 kV/mm @Frequency 60.0 Hz | 25.4 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 2.00 kV/mm @Frequency 60.0 Hz | 50.8 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Arc Resistance | 70 sec | 70 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 43.0 μm/m-°C | 23.9 μin/in-°F | ASTM E831 | ||
| CTE, linear, Transverse to Flow | 52.0 μm/m-°C | 28.9 μin/in-°F | ASTM E831 | ||
| Thermal Conductivity | 0.540 W/m-K | 3.75 BTU-in/hr-ft2-°F | ASTM C518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | As Molded; ASTM D648A | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Pellet | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||