- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.6
- 缺口沖擊強(qiáng)度: 0.251
- 彎曲強(qiáng)度 [MPa]: 52.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.570 g/cc | 0.0206 lb/in3 | ASTM D1895 |
| Water Absorption | 0.60 % | 0.60 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | ASTM D638 |
| Flexural Strength | 69.0 MPa | 10000 psi | |
| Compressive Strength | 189 MPa | 27400 psi | ASTM D695 |
| Shear Strength | 76.0 MPa | 11000 psi | as molded |
| Izod Impact, Notched | 0.251 J/cm | 0.470 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz | 4.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 12.8 kV/mm | 325 kV/in | Step by step; ASTM D149 |
| 14.7 kV/mm | 373 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 42.2 μm/m-°C @Temperature 23.0 - 60.0 °C | 23.4 μin/in-°F @Temperature 73.4 - 140 °F | |
| Specific Heat Capacity | 1.42 J/g-°C | 0.339 BTU/lb-°F | |
| Thermal Conductivity | 0.402 W/m-K | 2.79 BTU-in/hr-ft2-°F | |
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL temperature Index |
| Deflection Temperature at 1.8 MPa (264 psi) | 171 °C | 340 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | ||