- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 0.4
- 彎曲強度 [MPa]: 138.0
- 彎曲模量 [MPa]: 15.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.800 g/cc | 0.0289 lb/in3 | ASTM D1895 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ASTM D638 |
| Tensile Modulus | 18.6 GPa | 2700 ksi | ASTM D638 |
| Flexural Strength | 227 MPa | 32900 psi | |
| Flexural Modulus | 15.2 GPa | 2200 ksi | |
| Compressive Strength | 276 MPa | 40000 psi | ASTM D695 |
| Compressive Modulus | 10.5 GPa | 1530 ksi | @ 250°F |
| Shear Strength | 47.4 MPa | 6870 psi | |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.3 @Frequency 1e+6 Hz | 4.3 @Frequency 1e+6 Hz | ASTM D150 |
| 4.4 @Frequency 60 Hz | 4.4 @Frequency 60 Hz | ASTM D150 | |
| 4.4 @Frequency 1000 Hz | 4.4 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 15.7 kV/mm | 399 kV/in | Step by step; ASTM D149 |
| 17.7 kV/mm | 450 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | ASTM D150 |
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 | |
| 0.030 @Frequency 60 Hz | 0.030 @Frequency 60 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C @Thickness 3.00 mm | 302 °F @Thickness 0.118 in | |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||
| V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | ||