- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 0.03
- 缺口沖擊強度: 0.138
- 斷裂伸長率 [%]: 55.0
- 彎曲強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 - 1.99 g/cc | 0.0527 - 0.0719 lb/in3 | Average value: 1.58 g/cc Grade Count:32 |
| Water Absorption | 0.0300 - 0.290 % | 0.0300 - 0.290 % | Average value: 0.168 % Grade Count:25 |
| Linear Mold Shrinkage | 0.00180 - 0.00860 cm/cm | 0.00180 - 0.00860 in/in | Average value: 0.00530 cm/cm Grade Count:32 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 70.0 - 91.0 | 70.0 - 91.0 | Average value: 80.9 Grade Count:23 |
| Tensile Strength, Ultimate | 40.0 - 119 MPa | 5800 - 17300 psi | Average value: 53.1 MPa Grade Count:32 |
| Elongation at Break | 0.310 - 1.70 % | 0.310 - 1.70 % | Average value: 0.761 % Grade Count:32 |
| Modulus of Elasticity | 8.10 - 23.0 GPa | 1170 - 3340 ksi | Average value: 10.8 GPa Grade Count:32 |
| Flexural Yield Strength | 55.0 - 240 MPa | 7980 - 34800 psi | Average value: 92.9 MPa Grade Count:32 |
| Flexural Modulus | 6.00 - 21.0 GPa | 870 - 3050 ksi | Average value: 9.46 GPa Grade Count:32 |
| Compressive Yield Strength | 152 - 434 MPa | 22000 - 62900 psi | Average value: 199 MPa Grade Count:32 |
| Poissons Ratio | 0.270 - 0.350 | 0.270 - 0.350 | Average value: 0.331 Grade Count:14 |
| Shear Modulus | 3.00 - 5.82 GPa | 435 - 844 ksi | Average value: 3.73 GPa Grade Count:14 |
| Izod Impact, Notched | 0.138 - 0.243 J/cm | 0.259 - 0.455 ft-lb/in | Average value: 0.169 J/cm Grade Count:23 |
| Charpy Impact Unnotched | 0.600 - 1.36 J/cm2 | 2.86 - 6.47 ft-lb/in2 | Average value: 0.889 J/cm2 Grade Count:8 |
| Charpy Impact, Notched | 0.150 - 0.450 J/cm2 | 0.714 - 2.14 ft-lb/in2 | Average value: 0.211 J/cm2 Grade Count:32 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 2.10e+14 ohm-cm | 1.00e+11 - 2.10e+14 ohm-cm | Average value: 1.05e+13 ohm-cm Grade Count:26 |
| Insulation Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | Average value: 4.52e+10 ohm Grade Count:5 |
| Dielectric Constant | 4.40 - 6.10 | 4.40 - 6.10 | Average value: 5.33 Grade Count:24 |
| Dielectric Strength | 6.90 - 30.0 kV/mm | 175 - 762 kV/in | Average value: 14.3 kV/mm Grade Count:32 |
| Dissipation Factor | 0.0172 - 0.0820 | 0.0172 - 0.0820 | Average value: 0.0514 Grade Count:24 |
| Arc Resistance | 137 - 188 sec | 137 - 188 sec | Average value: 168 sec Grade Count:24 |
| Comparative Tracking Index | 150 - 225 V | 150 - 225 V | Average value: 177 V Grade Count:32 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 16.0 - 55.0 μm/m-°C | 8.89 - 30.6 μin/in-°F | Average value: 35.9 μm/m-°C Grade Count:9 |
| 21.0 - 82.0 μm/m-°C @Temperature 40.0 - 130 °C | 11.7 - 45.6 μin/in-°F @Temperature 104 - 266 °F | Average value: 50.5 μm/m-°C Grade Count:19 | |
| CTE, linear, Transverse to Flow | 24.0 - 65.0 μm/m-°C | 13.3 - 36.1 μin/in-°F | Average value: 46.1 μm/m-°C Grade Count:8 |
| Thermal Conductivity | 0.440 - 0.620 W/m-K @Temperature 100 - 100 °C | 3.05 - 4.30 BTU-in/hr-ft2-°F @Temperature 212 - 212 °F | Average value: 0.510 W/m-K Grade Count:14 |
| Maximum Service Temperature, Air | 190 - 232 °C | 374 - 450 °F | Average value: 208 °C Grade Count:24 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 - 250 °C | 302 - 482 °F | Average value: 180 °C Grade Count:32 |
| Deflection Temperature at 8.0 MPa | 130 - 178 °C | 266 - 352 °F | Average value: 147 °C Grade Count:7 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:31 |
| Oxygen Index | 26.4 - 45.0 % | 26.4 - 45.0 % | Average value: 33.8 % Grade Count:20 |
| Shrinkage | 0.0400 - 0.340 % | 0.0400 - 0.340 % | Average value: 0.176 % Grade Count:31 |